经销日本油墨耐化学尺寸稳定PPS FZ-6600
| 物理性能 | 比重 | ASTMD792 | 1.96 | g/cm³ | |
| 收缩率 | 流动 | ASTMD955 | 0.25 | % | |
| 横向流动 | ASTMD955 | 1.0 | % | ||
| 吸水率(23°C,24hr) | ASTMD570 | 0.020 | % | ||
| 硬度 | 洛氏硬度 | M级 | ASTMD785 | 100 | |
| R级 | ASTMD785 | 121 | |||
| 机械性能 | 拉伸模量 | ASTMD638 | 19000 | MPa | |
| 抗张强度 | ASTMD638 | 180 | MPa | ||
| 伸长率(断裂) | ASTMD638 | 1.2 | % | ||
| 弯曲模量 | ASTMD790 | 18000 | MPa | ||
| 弯曲强度 | ASTMD790 | 250 | MPa | ||
| 压缩强度 | ASTMD695 | 170 | MPa | ||
| 泊松比 | 0.34 | ||||
| 摩擦系数 | 与钢-动态 | ASTMD1894 | 0.35 | ||
| 与钢-静态 | ASTMD1894 | 0.35 | |||
| 断裂弯曲伸长率 | ASTMD790 | 1.8 | % | ||
| 冲击性能 | 悬壁梁缺口冲击强度 | ASTMD256 | 80 | J/m | |
| 无缺口悬臂梁冲击 | ASTMD256 | 450 | J/m | ||
| 热性能 | 载荷下热变形温度(1.8MPa,未退火) | ASTMD648 | 265 | °C | |
| 线形热膨胀系数 | 流动:-30到90°C | ASTMD696 | 1.7E-5 | cm/cm/°C | |
| 横向:-30到90°C | ASTMD696 | 1.7E-5 | cm/cm/°C | ||
| 电气性能 | 体积电阻率 | ASTMD257 | 1.0E+16 | ohms·cm | |
| 介电强度(1.60mm) | ASTMD149 | 16 | kV/mm | ||
| 介电常数(1MHz) | ASTMD150 | 5.00 | |||
| 耗散因数(1MHz) | ASTMD150 | 6.0E-3 | |||
| 耐电弧性 | ASTMD495 | 180 | sec | ||
| 漏电起痕指数 | ASTMD3638 | 250 | V | ||
| 可燃性 | UL阻燃等级(0.8mm) | UL94 | V-0 |
PPS的介电常数很小，介电损耗相当低，表面电阻率和体积电阻率对频率、温度、湿度的变化不敏感，是优良的电绝缘材料，它的耐电狐时间也较长，pps的化学稳定性相当好，除了受强氧化酸，如浓硫酸、浓硝酸和王水的侵蚀外，它不受绝大多数酸碱盐的侵蚀，具有接近于PTFE的化学稳定性。在低于175度时不溶于任何已知的有机溶剂，pps与一般有机溶剂接触时不会出现塑件开裂现象。