RytonR-4ChevronPhillipsChemicalCompanyLLCPPSRytonR-4-010BLChevronPhillipsChemicalCompanyLLCPPSRytonR-4-200BLChevronPhillipsChemicalCompanyLLCPPSRytonR-4-200NAChevronPhillipsChemicalCompanyLLCPPSRytonR-4-220BLChevronPhillipsChemicalCompanyLLCPPSRytonR-4-220NAChevronPhillipsChemicalCompanyLLCPPSRytonR-4-230BLChevronPhillipsChemicalCompanyLLCPPSRytonR-4-230NAChevronPhillipsChemicalCompanyLLCPPSRytonR-4-232NAChevronPhillipsChemicalCompanyLLCPPSRytonR-4-240BLChevronPhillipsChemicalCompanyLLCPPSRytonR-4-240NAChevronPhillipsChemicalCompanyLLCPPSRytonR-4XTChevronPhillipsChemicalCompanyLLCPPSRytonR-7-120BLChevronPhillipsChemicalCompanyLLCPPSRytonR-7-120NAChevronPhillipsChemicalCompanyLLCPPSRytonR-7-121BLChevronPhillipsChemicalCompanyLLCPPSRytonR-7-121NAChevronPhillipsChemicalCompanyLLCPPSRytonR-7-220BLChevronPhillipsChemicalCompanyLLCPPS
聚苯硫醚是一种结晶性的聚合物。未经拉伸的纤维具有较大的无定形区（结晶度约为5%），在125℃时发生结晶放热，玻璃化温度为93℃；熔点281℃。拉伸纤维在拉伸过程中产生了部分结晶，（增加至30%），如在130—230℃温度下对拉伸纤维进行热处理，可使结晶度增加到60—80%。因此，拉伸后的纤维没有明显的玻璃化转变或结晶放热现象，其熔点为284℃。随着拉伸热定形后结晶度的提高，纤维的密度也相应增大，由拉伸前的1.33g/cm3到拉伸后的1.34g/cm3，经热处理后则可达1.38g/cm3。
PPS是一种综合性能优异的特种工程塑料。PPS具有优良的耐高温、耐腐蚀、耐辐射、阻燃、均衡的物理机械性能和极好的尺寸稳定性以及优良的电性能等特点，被广泛用作结构性高分子材料，通过填充、改性后广泛用作特种工程塑料。同时，还可制成各种功能性的薄膜、涂层和复合材料，在电子电器、航空航天、汽车运输等领域获得成功应用。近年来，国内企业积极研发，并初步形成了一定的生产能力，改变了以往完全依赖进口的状况。但是，中国PPS技术还存在产品品种少、高功能产品少、产能急待扩大等问题，这些将是PPS下一步发展的重点。
pps具有机械强度高、耐高温、高阻燃、耐化学药品性能强等优点；具有硬而脆、结晶度高、难燃、热稳定性好、机械强度较高、电性能优良等优点。
PPS是工程塑料中耐热性的品种之一，热变形温度一般大于260度、抗化学性仅次于聚四氟乙烯，流动性仅次于尼龙。 此外，它还具有成型收缩率小（约0.8%），吸水率低（约0.02%），防火性好、耐震动疲乏性好等优点。⒈36克/立方厘米成型收缩率：0.7%成型温度：300-330℃。