SABICInnovative Plastics LNP LUBRICOMP DFL14 PC
Polymer,Thermoplastic,Polycarbonate (PC)
SABIC Innovative Plastics (GE Plastics)
产品说明:
LNP LUBRICOMP* DFL14 is a compound based on Polycarbonate resincontaining 20% Glass Fiber and 5% PTFE. Added features include:Internally Lubricated.
SABIC Innovative Plastics LNP LUBRICOMP DFL14 PC 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.38 g/cc | 1.38 g/cc | ASTM D792 |
| 密度 | 1.38 g/cc | 0.0499 lb/in³ | ASTM D792 |
| 水分吸收 | 0.120 % | 0.120 % | 50% RH, 24 hrs; ASTM D570 |
| 0.190 % | 0.190 % | 23°C / 50% RH; ISO 62 | |
| 线性成型收缩率,Flow | 0.0020 - 0.0040 cm/cm @Time 86400 sec | 0.0020 - 0.0040 in/in @Time 24.0 hour | ASTM D955 |
| 线性成型收缩率，横向 | 0.0050 - 0.0070 cm/cm @Time 86400 sec | 0.0050 - 0.0070 in/in @Time 24.0 hour | ASTM D955 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | 94.0 MPa | 13600 psi | Type I, 5 mm/min; ASTM D638 |
| 94.0 MPa | 13600 psi | 5 mm/min; ISO 527 | |
| 抗张强度(屈服) | 96.0 MPa | 13900 psi | Type I, 5 mm/min; ASTM D638 |
| 96.0 MPa | 13900 psi | 5 mm/min; ISO 527 | |
| 伸长率 (断裂) | 3.5 % | 3.5 % | 5 mm/min; ISO 527 |
| 3.8 % | 3.8 % | Type I, 5 mm/min; ASTM D638 | |
| 屈服伸长率 | 2.9 % | 2.9 % | 5 mm/min; ISO 527 |
| 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 | |
| 拉伸模量 | 6.02 GPa | 873 ksi | 1 mm/min; ISO 527 |
| 6.32 GPa | 917 ksi | 5 mm/min; ASTM D638 | |
| 弯曲强度 | 158 MPa | 22900 psi | ISO 178 |
| 161 MPa | 23400 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 165 MPa | 23900 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 弯曲模量 | 5.59 GPa | 811 ksi | 2 mm/min; ISO 178 |
| 5.82 GPa | 844 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 悬壁梁缺口冲击强度 | 1.70 J/cm | 3.18 ft-lb/in | ASTM D256 |
| 悬壁梁无缺口冲击强度 | 7.16 J/cm | 13.4 ft-lb/in | ASTM D4812 |
| 悬壁梁缺口冲击强度 | 15.0 kJ/m² | 7.14 ft-lb/in² | 80*10*4; ISO 180/1A |
| 悬壁梁无缺口冲击强度 | 54.0 kJ/m² |