DOWLEX™2607GC
Linear Low Density Polyethylene Resin
The Dow Chemical Company
产品说明：
DOWLEX 2607 GC Polyethylene Resin is specifically designed forlarge/high output cast film lines to make high performanceindustrial stretch films.
Films made from DOWLEX 2607 GC Polyethylene Resin exhibit anexcellent balance of processability, mechanical and stretchabilityperformance properties.
DOWLEX 2607 GC Polyethylene Resin is to be used as a core resin incoextruded cast film structures for films in the thickness rangebetween 10 and 35 microns.
Complies with:
EU, No10/2011
U.S. FDA FCN 741
Consult the regulations for complete details.
会员资料
| 公司名称: |
| 联系人: |
| 公司地址: |
| 完善资料 |
附加功能
| PDF物性文档 [普通版本] [带会员联系方式版本] |
| 查找替代物 |
| 加入收藏 |
DOWLEX™ 2607GC 物性表
| 基本信息 | |
|---|---|
| 机构评级 |
|
| 形式 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | 0.918 | g/cm³ | ASTM D792 |
| 熔流率（熔体流动速率） (190°C/2.16 kg) | 2.3 | g/10 min | ISO 1133 |
| 薄膜 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 薄膜厚度 - 经测试 | 23 | µm | |
| 膜刺穿强度 (23 µm) | 160 | J | |
| 膜刺穿力 (23µm) | 44.0 | N | |
| 抗张强度 | ASTM D882 | ||
| MD : 屈服, 23 µm | 8.00 | MPa | ASTM D882 |
| TD : 屈服, 23 µm | 8.00 | MPa | ASTM D882 |
| MD : 断裂, 23 µm | 35.0 | MPa | ASTM D882 |
| TD : 断裂, 23 µm | 29.0 | MPa | ASTM D882 |
| 伸长率 | ASTM D882 | ||
| MD : 断裂, 23 µm | 460 | % | ASTM D882 |
| TD : 断裂, 23 µm | 700 | % | ASTM D882 |
| 落锤冲击 (23µm) | 150 | g | ASTM D1709A |
| 埃尔曼多夫抗撕强度 | ASTM D1922 | ||
| MD : 23 µm | 190 | g | ASTM D1922 |
| TD : 23 µm | 420 | g | ASTM D1922 |
| 薄膜拉伸性能 - 大拉伸力 (23.0 µm) | 37000 | g | 内部方法 |
| 薄膜拉伸性能 - 大伸长率 (23.0 µm) | 350 | % | 内部方法 |
| 补充信息 |
|---|