LG Chemical HIPS 405AF PS, Flame Retardant 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.16 g/cc | 1.16 g/cc | ASTM D792 |
| 处理 | 0.010 | 0.010 | Injection Molding |
| 线性成型收缩率,Flow | 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm | 0.0040 - 0.0080 in/in @Thickness 0.126 in | ASTM D955 |
| 熔体流动速率 | 15 g/10 min @Load 5.00 kg, Temperature 200 °C | 15 g/10 min @Load 11.0 lb, Temperature 392 °F | ASTM D1238 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 洛氏硬度（R 级） | 90 | 90 | ASTM D785 |
| 抗张强度(屈服) | 25.5 MPa @Thickness 3.20 mm | 3700 psi @Thickness 0.126 in | 50mm/min; ASTM D638 |
| 伸长率 (断裂) | 60 % @Thickness 3.20 mm | 60 % @Thickness 0.126 in | 50mm/min; ASTM D638 |
| 屈服伸长率 | >= 5.0 % @Thickness 3.20 mm | >= 5.0 % @Thickness 0.126 in | 50mm/min; ASTM D638 |
| 弯曲强度 | 43.1 MPa @Thickness 3.20 mm | 6260 psi @Thickness 0.126 in | 15mm/min; ASTM D790 |
| 弯曲模量 | 2.16 GPa @Thickness 3.20 mm | 313 ksi @Thickness 0.126 in | 15mm/min; ASTM D790 |
| 悬壁梁缺口冲击强度 | 0.392 J/cm @Thickness 3.20 mm, Temperature -30.0 °C | 0.735 ft-lb/in @Thickness 0.126 in, Temperature -22.0 °F | ASTM D256 |
| 0.392 J/cm @Thickness 6.40 mm, Temperature -30.0 °C | 0.735 ft-lb/in @Thickness 0.252 in, Temperature -22.0 °F | ASTM D256 | |
| 0.785 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |