Daikin POLYFLON MG-1050F PTFE 25% Glass Fiber Filled MoldingPowder, High Apparent Density, Free Flow 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 2.13 - 2.22 g/cc | 2.13 - 2.22 g/cc | ASTM D792 |
| 吸水率 | 0.00 % @Thickness 8.50 mm, Time 86400 sec | 0.00 % @Thickness 0.335 in, Time 24.0 hour | ASTM D570 |
| 粘度 | 1.00e+13 - 1.00e+15 cP @Temperature 340 - 380 °C | 1.00e+13 - 1.00e+15 cP @Temperature 644 - 716 °F | Melt viscosity |
| 线性成型收缩率 | 0.020 - 0.050 cm/cm | 0.020 - 0.050 in/in | |
| 变形 | 5.0 % | 5.0 % | 6.7 MPa load, at 100°C, 24 hrs; ASTM D621 |
| 7.0 % | 7.0 % | 13.7 MPa load, at 25°C, 24 hrs; ASTM D621 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 肖氏硬度 (邵氏 D) | 50 - 65 | 50 - 65 | |
| 抗张强度(断裂) | 20.0 - 45.0 MPa | 2900 - 6530 psi | ASTM D638 |
| 伸长率 (断裂) | 200 - 450 % | 200 - 450 % | ASTM D638 |
| 拉伸模量 | 0.392 GPa | 56.9 ksi | ASTM D638 |
| 弯曲模量 | 0.490 - 0.588 GPa | 71.1 - 85.3 ksi | ASTM D790 |
| 抗压强度 | 5.00 - 6.00 MPa @Temperature 25.0 °C | 725 - 870 psi @Temperature 77.0 °F | 1% deformation; ASTM D695 |
| 悬壁梁无缺口冲击强度 | 1.60 J/cm | 3.00 ft-lb/in | ASTM D256 |
| 摩擦系数 | 0.15 - 0.30 | 0.15 - 0.30 | Non-lubricating |
| 静态摩擦系数 | 0.020 | 0.020 | Coated-steel surface |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | <= 1.00e+18 ohm-cm | <= 1.00e+18 ohm-cm | ASTM D257 |
| 介电常数 | 2.1 |