PA12 瑞士EMS LCZ-15H增强级 耐 磨 耐候 耐高 温 阻燃尼龙PA12

机械性能测试条件测试方法数值/描述单位拉伸强度
ASTM D412/ISO 527120kg/cm²(MPa)[Lb/in²]断裂伸长率
ASTM D412/ISO 5270.3%拉伸模量
ASTM D412/ISO 527
kg/cm²(MPa)[Lb/in²]伸长率
ASTM D412/ISO 527
%弯曲模量
ASTM D412/ISO 527
kg/cm²(MPa)[Lb/in²]弯曲强度
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]洛氏硬度
ASTM D785

IZOD 缺口冲击强度1/4" 23℃ASTM D256/ISO 17912kg·cm/cm(J/M)ft·lb/in1/4"-30℃ASTM D256/ISO 17912kg·cm/cm(J/M)ft·lb/in1/8" 23℃ASTM D256/ISO17914kg·cm/cm(J/M)ft·lb/in1/8" -30℃ASTM D256/ISO17915kg·cm/cm(J/M)ft·lb/inCharpy冲击强度23℃ （缺口）ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in-30℃（缺口）ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in23℃（无缺口）ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in-30℃（无缺口）ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in拉伸断裂伸长率(延伸率)
ASTM D412/ISO 527
%物性性能测试条件测试方法数值/描述单位比重（密度）
ASTM D792/ISO 11831.12kg·cm/cm(J/M)ft·lb/in成型收缩率
ASTM D9550.02%熔融指数（流动系数）200℃/5kgASTM D1238/ISO11335g/10min220℃/10kgASTM D1238/ISO 11335g/10min吸水率 23℃/24H
ASTM D570/ISO 620.3%热性能测试条件测试方法数值/描述单位热变形温度退火ASTM D648/ISO75150℃（℉）未退火ASTM D648/ISO 75135℃（℉）维卡软化点
ASTM D1525/ISO R306155℃（℉）熔点
-215℃（℉）燃烧性（率）
UL94HB
线性膨胀系数
ASTM D696/ISO 11359
mm/mm.℃其他测试条件测试方法数值/描述单位备注
颜色黑色特性耐磨用途
电气性能测试条件测试方法数值/描述单位介电常数100HZASTM D150/IEC 60250

1MHZASTM D150/IEC 60250

体积电阻率
ASTM D257/IEC 60093
Ω.cm表面电阻率
ASTM D257/IEC 60093
Ω耐电弧性
ASTM D495/IEC 60112

介电损耗100HZASTM D150/IEC 60250

1MHZASTM D150/IEC 60250

加工条件测试条件测试方法数值/描述单位干燥条件



加工温度射嘴

℃料筒前段

℃料筒中段

℃料筒后段

℃熔体温度

210℃模具温度


℃压力注塑压力

Mpa保压压力

Mpa背压

Mpa螺杆转速

500rpm

瑞士EMS PA12 LCZ-15H 的优点：
瑞士EMS PA12LCZ-15H具有良好的加工工艺性能，低吸水性、柔软性、韧性、耐磨性、自润滑性具佳，超高温超低温性及抗化学腐蚀性能优良等性能。典型应用范围精密机械部件,电线电缆绝缘层,工具架,线圈。物性除具有一般PA特点外，还具有相对宽度小、吸水性低、尺寸稳定性好的优点，有较高的拉伸强度和冲击强度。
PA12是很好的电气绝缘体并且和其它聚酰胺一样不会因潮湿影响绝缘性能。它有很好的抗冲击性机化学稳定性。PA12有许多在塑化特性和增强特性方面的改良品种。和PA6及PA66相比这些材料有较低的熔点和密度具有非常高的回潮率。PA12对强氧化性酸无抵抗能力。PA12的粘性主要取决于湿度、温度和储藏时间。它的流动性很好。收缩率在0.5%到2%之间这主要取决于材料{TodayHot}品种、壁厚及其它工艺条件。