PA66美国首诺41SP 产品信息:
物理性能额定值 (公制)额定值 (英制)测试方法比重1.14 g/cc1.14 g/ccISO 1183吸水率1.2 %1.2 %24hrs; ISO 62平衡吸湿2.4 %2.4 %Equilibrium at 50%rh; ISO 62线性成型收缩率0.014cm/cm@Thickness 2.00 mm
0.014 in/in@Thickness 0.0787 in
ISO 294-4线性成型收缩率,横向0.016 cm/cm@Thickness 2.00 mm
0.016 in/in@Thickness 0.0787 in
ISO 294-4机械性能额定值 (公制)额定值 (英制)测试方法抗张强度(断裂)75.0 MPa10900 psiISO527-2抗张强度(屈服)98.0 MPa14200 psiISO 527-2伸长率 (断裂)13 %13 %ISO527-2屈服伸长率4.5 %4.5 %ISO 527-2拉伸模量3.80 GPa551 ksiISO 527-2弯曲强度100MPa14500 psiISO 178弯曲模量3.20 GPa464 ksiISO 178泊松比0.400.40ISO527-2悬壁梁缺口冲击强度6.00 kJ/m22.86 ft-lb/in2ISO 1805.00 kJ/m2
@Temperature -30.0 °C
2.38 ft-lb/in2@Temperature -22.0 °F
ISO 180简支梁无缺口冲击强度NB@Temperature 23.0 °C
NB@Temperature 73.4 °F
ISO 179/1eUNB
@Temperature -30.0 °C
NB@Temperature -22.0 °F
ISO 179/1eU简支梁缺口冲击强度0.500 J/cm2@Temperature -30.0 °C
ISO 179/1eA0.600 J/cm2
@Temperature 23.0 °C
2.86 ft-lb/in2@Temperature 73.4 °F
ISO 179/1eA电气性能额定值 (公制)额定值 (英制)测试方法体积电阻率1.00e 10 ohm-cm@Thickness 0.750 mm
1.00e 10 ohm-cm@Thickness 0.0295 in
IEC 60093介电强度26.0 kV/mm@Thickness 1.00 mm
660 kV/in@Thickness 0.0394 in
IEC 60243耐电弧性120 - 179 sec@Thickness 3.00 mm
120 - 179 sec@Thickness 0.118 in
ASTM D495相比耐漏电起痕指数(CTI)600 V@Thickness 3.00 mm
600 V@Thickness 0.118 in
IEC 60112热丝引燃 (HWI)7.0 - 14 sec@Thickness 0.710 mm
7.0 - 14 sec@Thickness 0.0280 in
UL 74615 - 29 sec
@Thickness 1.50 mm
15 - 29 sec@Thickness 0.0591 in
UL 74615 - 29 sec
@Thickness 3.00 mm
15 - 29 sec@Thickness 0.118 in
UL 746高电弧燃烧指数(HAI)>= 120 arcs@Thickness 0.710 mm
>= 120 arcs@Thickness 0.0280 in
UL 746>= 120 arcs
@Thickness 1.50 mm
>= 120 arcs@Thickness 0.0591 in
UL 746>= 120 arcs
@Thickness 3.00 mm
>= 120 arcs@Thickness 0.118 in
UL 746高压电弧跟踪率,HVTR0.000 - 10.0 mm/min0.000 - 0.394 in/minUL746热性能额定值 (公制)额定值 (英制)测试方法线性热膨胀系数10.0 μm/m-°C@Thickness 2.00 mm, Temperature 23.0 - 55.0 °C
5.56 μin/in-°F@Thickness 0.0787 in, Temperature 73.4 - 131 °F
ISO 11359-2线性热膨胀系数,横向流动10.0 μm/m-°C@Thickness 2.00 mm, Temperature 23.0 - 55.0 °C
ISO 11359-2熔融温度260 °C500 °FISO 11359-2载荷下热变形温度(0.46 MPa)230 °C446°FUnannealed; ISO 75-2/B载荷下热变形温度(1.8 MPa)90.0 °C194 °FUnannealed;ISO 75-2/AUL RTI130 °C@Thickness 0.400 mm
266 °F@Thickness 0.0157 in
UL 746130 °C
@Thickness 0.710 mm
266 °F@Thickness 0.0280 in
UL 746130 °C
@Thickness 1.50 mm
266 °F@Thickness 0.0591 in
UL 746130 °C
@Thickness 3.00 mm
266 °F@Thickness 0.118 in
UL 746UL RTI,机械冲击75.0 °C@Thickness 0.400 mm
167 °F@Thickness 0.0157 in
UL 74675.0 °C
@Thickness 0.710 mm
167 °F@Thickness 0.0280 in
UL 74675.0 °C
@Thickness 1.50 mm
167 °F@Thickness 0.0591 in
UL 74675.0 °C
@Thickness 3.00 mm
167 °F@Thickness 0.118 in
UL 746UL RTI,机械无冲击75.0 °C@Thickness 0.400 mm
UL 74685.0 °C
@Thickness 0.710 mm
185 °F@Thickness 0.0280 in
UL 74685.0 °C
@Thickness 1.50 mm
185 °F@Thickness 0.0591 in
UL 74685.0 °C
@Thickness 3.00 mm
185 °F@Thickness 0.118 in
UL 746可燃性(UL94)V-2@Thickness 0.400 mm
V-2@Thickness 0.0157 in
V-2
@Thickness 0.710 mm
V-2@Thickness 0.0280 in
V-2
@Thickness 1.50 mm
V-2@Thickness 0.0591 in
V-2
@Thickness 3.00 mm
V-2@Thickness 0.118 in
极限氧指数26 %26 %ISO 4589-2灼热丝易燃指数700 °C
@Thickness 0.710 mm
1290 °F@Thickness 0.0280 in
Ignition Temp; IEC 60695-2-12700 °C
@Thickness 1.50 mm
1290 °F@Thickness 0.0591 in
Ignition Temp; IEC 60695-2-12700 °C
@Thickness 3.00 mm
1290 °F@Thickness 0.118 in
Ignition Temp; IEC 60695-2-12800 °C
@Thickness 0.710 mm
1470 °F@Thickness 0.0280 in
Flammability Index; IEC 60695-2-12800 °C
@Thickness 1.50 mm
1470 °F@Thickness 0.0591 in
Flammability Index; IEC 60695-2-12930 °C
@Thickness 3.00 mm
1710 °F@Thickness 0.118 in
Flammability Index; IEC 60695-2-12加工性能额定值 (公制)额定值 (英制)测试方法加工温度285 -300 °C545 - 572 °FMelt料筒后部温度260 - 280 °C500 - 536 °F料筒中部温度270 - 285 °C518 - 545 °F
料筒前部温度280 - 290 °C536 - 554 °F
射嘴温度280 - 300 °C536 - 572 °F
模具温度65.0 - 95.0 °C149 - 203 °F
干燥温度<= 70.0 °C<= 158 °F