防火原材料 ABS AF360C ABS 韩国LG
LG ChemicalAF360C ABS, TBBA-free Flame Retardant, High Flow
Acrylonitrile Butadiene Styrene (ABS), Molded
LG Chemical
产品说明：
Feature: Injection Molding, TBBA-free Flame Retardant, HighFlow
Application: Electric/Electronic Applications (TV, Monitor Housing)IT/OA device
CASNo. 9003-56-9 and 1309-64-4
Information provided by LG Chemical
物性信息：
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| 处理 | 0.010 | 0.010 | Injection Molding |
| 线性成型收缩率,Flow | 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm | 0.0040 - 0.0070 in/in @Thickness 0.126 in | ASTM D955 |
| 熔体流动速率 | 40 g/10 min @Load 10.0 kg, Temperature 220 °C | 40 g/10 min @Load 22.0 lb, Temperature 428 °F | ASTM D1238 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 洛氏硬度（R 级） | 101 | 101 | ASTM D785 |
| 抗张强度(屈服) | 39.2 MPa @Thickness 3.20 mm | 5690 psi @Thickness 0.126 in | 50 mm/min; ASTM D638 |
| 伸长率 (断裂) | 20 % @Thickness 3.20 mm | 20 % @Thickness 0.126 in | 50 mm/min; ASTM D638 |
| 屈服伸长率 | >= 5.0 % @Thickness 3.20 mm | >= 5.0 % @Thickness 0.126 in | 50 mm/min; ASTM D638 |
| 拉伸模量 | 2.26 GPa @Thickness 3.20 mm | 327 ksi @Thickness 0.126 in | 1 mm/min; ASTM D638 |
| 弯曲强度 | 68.6 MPa @Thickness 6.40 mm | 9960 psi @Thickness 0.252 in | 15 mm/min; ASTM D790 |
| 弯曲模量 | 2.40 GPa @Thickness 6.40 mm | 348 ksi @Thickness 0.252 in | 15 mm/min; ASTM D790 |
| 悬壁梁缺口冲击强度 | 1.67 J/cm @Thickness 6.40 mm, Temperature 23.0 °C | 3.12 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F | ASTM D256 |
| 1.96 J/cm @Thickness 3.20 mm, Temperature 23.0 °C | 3.67 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F | ASTM D256 | |
| Izod Impact, Unnotched | 0.686 J/cm @Thickness 6.40 mm, Temperature -30.0 °C | 1.29 ft-lb/in @Thickness 0.252 in, Temperature -22.0 °F | ASTM D256 |
| 0.686 J/cm @Thickness 3.20 mm, Temperature -30.0 °C | 1.29 ft-lb/in @Thickness 0.126 in, Temperature -22.0 °F | ASTM D256 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 载荷下热变形温度(0.46 MPa) | 88.0 °C @Thickness 6.40 mm | 190 °F @Thickness 0.252 in | Unannealed; ASTM D648 |
| 载荷下热变形温度(1.8 MPa) | 81.0 °C @Thickness 6.40 mm | 178 °F @Thickness 0.252 in | Unannealed; ASTM D648 |
| 维卡软化温度 | 87.0 °C @Load 5.00 kg | 189 °F @Load 11.0 lb | 50°C/h; ASTM D1525 |
| UL RTI | 60.0 °C | 140 °F | UL 746B |
| UL RTI，机械冲击 | 60.0 °C | 140 °F | UL 746B |
| UL RTI，机械无冲击 | 60.0 °C | 140 °F |