性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |||
基本性能 | 吸水率 | ASTM D-570 | 0.15 | % | |||
熔融指数 | ASTM D-1238 | 17.5 | g/10min | ||||
物理性能 | 比重 | ASTM D-792 | 1.2 | ||||
模具收缩率 | 3.2mm | ASTM D-955 | 5-7 | 10× | |||
机械性能 | 弯曲模量 | ASTM D-790 | 2343 | MPa | |||
拉伸强度 | 屈伏点 | ASTM D-638 | 62 | MPa | |||
拉伸率 | 断裂点 | ASTM D-638 | 125 | % | |||
冲击强度 | 缺口23°C | ASTM D-256 | 693 | J/M | |||
洛氏硬度 | ASTM D-785 | 118 | |||||
弯曲强度 | ASTM D-790 | 96 | MPa | ||||
拉伸强度 | 断裂点 | ASTM D-638 | 69 | MPa | |||
电气性能 | 损耗因数 | 1MHz | ASTM D-150 | 0.01 | |||
介电常数 | 1MHz | ASTM D-150 | 2.96 | ||||
60Hz | ASTM D-150 | 3.17 | |||||
体积电阻率 | ASTM D-257 | 1.0×10 | Ω.cm | ||||
损耗因数 | 60Hz | ASTM D-150 | 0.0009 | ||||
热性能 | 热变形温度 | ASTM D-648 | 129 | °C | |||
UL长期使用温度 | UL746B | 130 | °C | ||||
线膨胀系数 | ASTM E-831 | 6.8×10 | 1/°C | ||||
阻燃性 | UL 94 | HB | |||||
热变形温度 | 0.45MPa | ASTM D-648 | 137 | °C | |||
维卡软化点 | ASTM D-1525 | 154 | °C | ||||
阻燃性 | UL 94 | 1.1 | mm |