PC/日本帝人/G-3430H/玻纤增强30%/表面光洁/易脱模
PC/日本帝人/G-3430H/玻纤增强30%/表面光洁/易脱模
PC/日本帝人/G-3430H/玻纤增强30%/表面光洁/易脱模
PC/日本帝人/G-3430H/玻纤增强30%/表面光洁/易脱模
PC/日本帝人/G-3430H/玻纤增强30%/表面光洁/易脱模
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 吸水率 | 24hr，in 23℃ | ASTM D-570 | 0.12 | % | |
| 物理性能 | 比重 | JIS K-7112 | 1.43 | |||
| 阻燃性 | 3.0mm | UL 94 | V-1 | |||
| 阻燃性 | 0.8mm | UL 94 | V-2 | |||
| 阻燃性 | 0.43mm | UL 94 | HB | |||
| 机械性能 | 压缩强度 | ASTM D-695 | 129(1320) | Mpa(kgf/cm2) | ||
| 弯曲模量 | ASTM D-790 | 6380(65000) | Mpa(kgf/cm2) | |||
| 洛氏硬度 | ASTM D-785 | 93 | M标度 | |||
| 拉伸模量 | ASTM D-638 | 6080(62000) | Mpa(kgf/cm2) | |||
| 拉伸强度 | ASTM D-638 | 108(1100) | Mpa(kgf/cm2) | |||
| 断裂伸长率 | ASTM D-638 | 3.0 | % | |||
| 耐冲击强度值 | 艾氏、带缺口厚度3.2mm | ASTM D-256 | 88(9) | J/m(kgf·cm/cm) | ||
| 耐冲击强度值 | 艾氏、带缺口厚度6.4mm | ASTM D-256 | 88(9) | J/m(kgf·cm/cm) | ||
| 弯曲强度 | ASTM D-790 | 152(1550) | Mpa(kgf/cm2) | |||
| 电气性能 | 耐电弧性 | ASTM D-495 | 100 | sec | ||
| 介电正切 | 106Hz | ASTM D-150 | 0.009 | |||
| 介电率 | 106Hz | ASTM D-150 | 3.41 | |||
| 缘破坏强度 | 快速加压值厚度1.6mm | ASTM D-149 | 30 | kv/mm | ||
| 介电正切 | 60Hz | ASTM D-150 | 0.0009 | |||
| 体积电阻率 | ASTM D-257 | 1×1016 | Ω.cm | |||
| 介电率 | 60Hz | ASTM D-150 | 3.51 | |||
| 耐导电径迹性（CTI） | IEC 112 | 180 | V | |||
| 加工性能 | 成型收缩率 | 流动方向 | ASTM D-955 | 0.1～0.3 | % | |
| 垂直方向 | ASTM D-955 | 0.3～0.5 | % | |||
| 热性能 | 温度指数 | 电学式 | 厚度1.47mm | UL 746B | 130 | ℃ |
| 冲击式 | 厚度1.47mm | UL 746B | 125 | ℃ | ||
| 非冲击式 | 厚度1.47mm | UL 746B | 130 | ℃ | ||
| 负荷挠曲温度 | 负荷1.813MPa(18.6kgf/cm2) | JIS K-7207 | 142 | ℃ | ||
| 负荷挠曲温度 | 负荷0.451MPa(4.6kgf/cm2) | JIS K-7207 | 146 | ℃ | ||
| 线膨胀系数 | 流动方向 | ASTM D-696 | 3.2 | 10-5cm/cm/℃ | ||
| 垂直方向 | ASTM D-696 | 5.6 | 10-5cm/cm/℃ | |||